ALLOY NO.
|
NAME
|
NOMINAL COMPOSITION (PERCENT)
|
TENSILE STRENGTH
|
YIELD STRENGTH@7.5% EXTENSION UNDER LOAD (KSI) (a)
|
ELONGATION % IN 2 IN. (UNLESS OTHERWISE SPECIFIED)
|
ROCKWELL HARNESS NO.
|
MELTING POINTC (LIQUIDS)
|
DENSITY (LBS./CU.IN.)
|
AVERAGE COEFFICIENT LINEAR THERMAL EXPANSION PER F(77-572F)
|
ELECTRICAL CONDUCT.% IACS@ 68 VOLUMETRIC (C)
|
THERMAL CONDUCT. BTU/FT.2/FT/HR/F@ 68
|
ALLOY NO.
|
|
|
|
COPPER
|
ZINC
|
TIN
|
LEAD
|
IRON
|
PHOS-PHORUS
|
OTHER
|
HARD (b)
|
SOFT
|
HARD (b)
|
SOFT
|
HARD (b)
|
SOFT
|
HARD (b)
|
SOFT
|
|
|
|
|
|
|
|
C10200
|
OXYGEN-FREE HIGH CONDUCTIVITY COPPER
|
99.99 (+)
|
|
|
|
|
|
|
45
|
33
|
40
|
10
|
10
|
45
|
B45
|
F45
|
1083
|
0.323
|
0.0000098
|
101.0
|
226
|
C10200
|
|
C10400
|
OXYGEN-FREE WITH SILVER 8 OZ/TON
|
99.99 (+)
|
|
|
|
|
|
8 OZ. Ag (d)
|
55
|
32
|
50
|
7.5
|
8
|
45
|
B60
|
F40
|
1083
|
0.323
|
0.0000098
|
100.0
|
224
|
C10400
|
|
C10500
|
OXYGEN-FREEW ITH SILVER 10 OZ/TON
|
99.95 (+)
|
|
|
|
|
|
10 OZ. Ag (d)
|
55
|
32
|
50
|
7.5
|
8
|
45
|
B60
|
F40
|
1083
|
0.323
|
0.0000098
|
100.0
|
224
|
C10500
|
|
C10700
|
OXYGEN-FREE WITH SILVER 25 OZ/TON
|
99.95 (+)
|
|
|
|
|
|
25 OZ. Ag (d)
|
55
|
32
|
50
|
7.5
|
8
|
45
|
B60
|
F40
|
1083
|
0.323
|
0.0000098
|
100.0
|
224
|
C10700
|
|
C11000
|
ELECTROLYTIC TOUGH PITCH COPPER
|
99.9 (+)
|
|
|
|
|
|
|
50
|
34
|
45
|
11
|
6
|
45
|
B50
|
F45
|
1083
|
0.323
|
0.0000098
|
101.0
|
226
|
C11000
|
|
C12000
|
PHOSPHORUS DEOXIDIZED, LOW RESIDUAL PHOSPHORUS
|
99.9 (+)
|
|
|
|
|
0.006
|
|
55
|
34
|
50
|
11
|
8
|
45
|
B60
|
F45
|
1083
|
0.323
|
0.0000098
|
97.0
|
219
|
C12000
|
|
C12200
|
PHOSPHORUS DEOXIDIZED, HIGH RESIDUE PHOSPHORUS
|
99.9 (+)
|
|
|
|
|
0.025
|
|
45
|
33
|
40
|
1
|
10
|
45
|
B40
|
F45
|
1083
|
0.323
|
0.0000098
|
85.0
|
196
|
C12200
|
|
C14200
|
PHOSPHORIZED ARSENICAL COPPER
|
99.68
|
|
|
|
|
|
|
45
|
33
|
40
|
10
|
10
|
45
|
B50
|
F45
|
1080
|
0.323
|
0.0000098
|
45.0
|
112
|
C14200
|
|
C19200
|
IRON COPPER 192
|
98.97
|
|
|
|
1.0
|
0.03
|
|
56
|
37
|
52
|
12
|
7
|
40
|
|
|
1084
|
0.320
|
0.000009
|
50.0
|
125
|
C19200
|
|
C19400
|
IRON COPPER 194
|
97.43
|
0.13
|
|
|
2.4
|
0.04
|
|
68
|
45
|
64
|
26
|
2
|
28
|
B73
|
B38
|
1090
|
0.317
|
0.000009
|
65.0
|
150
|
C19400
|
|
C2200
|
COMMERCIAL BRONZE
|
90.00
|
10.00
|
|
|
|
|
|
62
|
38
|
50
|
12
|
6
|
48
|
B70
|
B1
|
1045
|
0.318
|
0.0000101
|
44.0
|
109
|
C2200
|
|
C2300
|
RED BRASS 85%
|
85.00
|
15.00
|
|
|
|
|
|
65
|
45
|
53
|
15
|
10
|
50
|
B72
|
B5
|
1025
|
0.316
|
0.0000104
|
37.0
|
92
|
C2300
|
|
C2400
|
LOW BRASS 80%
|
80.00
|
20.00
|
|
|
|
|
|
74
|
48
|
59
|
17
|
7
|
47
|
B82
|
F69
|
1000
|
0.313
|
0.0000106
|
32.5
|
81
|
C2400
|
|
C2600
|
CARTRIDGE BRASS 70%
|
70.00
|
30.00
|
|
|
|
|
|
76
|
47
|
62
|
17
|
10
|
60
|
B83
|
B15
|
955
|
0.308
|
0.0000111
|
28.0
|
70
|
C2600
|
|
C27200
|
YELLOW BRASS 272
|
63.50
|
36.50
|
|
|
|
|
|
70
|
45
|
60
|
16
|
12
|
55
|
B80
|
F70
|
925
|
0.306
|
0.0000114
|
26.0
|
67
|
C27200
|
|
C27400
|
YELLOW BRASS 274
|
63.00
|
37.00
|
|
|
|
|
|
65
|
46
|
50
|
17
|
10
|
55
|
B75
|
B20
|
920
|
0.305
|
0.0000114
|
26.0
|
67
|
C27400
|
|
C28000
|
MUNTZ METAL
|
60.00
|
40.00
|
|
|
|
|
|
74
|
56
|
55
|
23
|
10
|
50
|
|
B45
|
905
|
0.303
|
0.0000116
|
28.4
|
72
|
C28000
|
|
C33000
|
LOW LEADED BRASS
|
66.50
|
33.00
|
|
0.50
|
|
|
|
73
|
45
|
60
|
17
|
10
|
55
|
B80
|
B15
|
935
|
0.307
|
0.0000112
|
26.0
|
67
|
C33000
|
|
C33100
|
LEADED BRASS
|
66.00
|
33.00
|
|
1.00
|
|
|
|
73
|
45
|
60
|
17
|
10
|
55
|
B80
|
B15
|
935
|
0.307
|
0.0000112
|
26.0
|
67
|
C33100
|
|
C33200
|
FREE CUTTING BRASS
|
66.50
|
31.90
|
|
1.60
|
|
|
|
73
|
45
|
60
|
17
|
10
|
50
|
B80
|
B15
|
935
|
0.307
|
0.0000113
|
26.0
|
67
|
C33200
|
|
C43500
|
TRUMPET BRASS
|
81.00
|
18.00
|
|
1.00
|
|
|
|
70
|
45
|
60
|
16
|
15
|
60
|
B78
|
B15
|
1005
|
0.313
|
0.0000108
|
27.5
|
70
|
C43500
|
|
C44300
|
ARSENICAL ADMIRALITY
|
71.00
|
27.96
|
|
1.00
|
|
|
As,.04
|
|
52
|
|
20
|
|
60
|
|
B30
|
935
|
0.308
|
0.0000112
|
25.0
|
64
|
C44300
|
|
C46400
|
NAVAL BRASS
|
60.00
|
39.25
|
|
0.75
|
|
|
|
88
|
|
66
|
|
18
|
|
|
|
895
|
0.304
|
0.0000118
|
26.0
|
67
|
C46400
|